Hostaform? LX90Z XAP2 ?

Acetal (POM) Copolymer

Celanese Corporation

產(chǎn)品說明：

Preliminary Data Sheet

Hostaform? acetal copolymer grade LX90Z XAP2 ? is UV stabilized material available in a range of molded in metallic colors generally for automotive interior applications. In addition, Hostaform? LX90Z XAP2 ? has lower volatile emissions as required for some automotive interiors.

Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Celanese Technical Service for assistance with your application.

Low Emission Performance [VDA-275]

紫外線穩(wěn)定劑

特性

低揮發(fā)

用途

汽車領(lǐng)域的應(yīng)用

汽車內(nèi)部零件

RoHS 合規(guī)性

聯(lián)系制造商

外觀

金屬化 - 染色

可用顏色

物理性能額定值單位制測(cè)試方法

密度	1.43	g/cm3	ISO 1183
溶化體積流率（MVR） (190°C/2.16 kg)	8.00	cm3/10min	ISO 1133
收縮率			ISO 294-4
垂直流動(dòng)方向	1.4	%	ISO 294-4
流動(dòng)方向	2.3	%	ISO 294-4
吸水率 (飽和, 23°C)	0.75	%	ISO 62

機(jī)械性能額定值單位制測(cè)試方法

拉伸模量	2700	MPa	ISO 527-2/1A/1
拉伸應(yīng)力 (屈服)	54.0	MPa	ISO 527-2/1A/50
拉伸應(yīng)變 (屈服)	8.0	%	ISO 527-2/1A/50
彎曲模量 (23°C)	2900	MPa	ISO 178

沖擊性能額定值單位制測(cè)試方法

簡(jiǎn)支梁缺口沖擊強(qiáng)度			ISO 179/1eA
-30°C	4.0	kJ/m2	ISO 179/1eA
23°C	4.0	kJ/m2	ISO 179/1eA

熱性能額定值單位制測(cè)試方法

熱變形溫度
0.45 MPa, 未退火	147	°C	ISO 75-2/B
1.8 MPa, 未退火	90.0	°C	ISO 75-2/A
熔融溫度 1	166	°C	ISO 11357-3
線形熱膨脹系數(shù)			ISO 11359-2
流動(dòng)	9.0E-5	cm/cm/°C	ISO 11359-2
橫向	1.0E-4	cm/cm/°C	ISO 11359-2